the ingot internal uniformity, which is mainly determined by the initial solidification processes. The imperfection of the casting process control at the initial section "ladle-tundish-mold", especially the mold level, leads to occurrence of internal nonuniformity and surface defects, as well as distortion of the slab shape. Thus, the level drop below setting value leads to inner surface oxidation of the formed ingot crust and its structural nonuniformity. If metal level increases, overflow over the ingot crust occurs, which leads to increase the oscillation traces depth and capture of non-metallic and slag inclusions. Therefore, the mold is the most important technological element of the continuous casting machine (CCM). The scientific and technical complexity of the mold level control problem is the lack of technical capability of the metal level measuring in real technological conditions with the required accuracy, as well as changes in the object parameters during operation and in non-stationary modes. The modernization of existing control systems through the introduction of new control algorithms is one of the ways to improve the efficiency of the metal level stabilization control in the continuous casting machine mold. It demands to single out the factors affecting the metal level stability in order to observe and compensate them. In this paper implementation of the combined control principle based on the main disturbances compensation and controlled coordinate feedback is proposed. The synthesis of static compensators with constant and variable compensation coefficients was carried out in accordance with the principle of invariance, which allows to significantly reduce the deviation of the controlled variable in nonstationary operating modes.